Insulation articles including corrosion inhibitors and methods of producing the same

ABSTRACT

Unique insulation articles including corrosion inhibitors and methods of producing the same are disclosed. One exemplary embodiment is an article of manufacture comprising an insulation mat comprising a cured combination of a plurality of randomly oriented fibers and a binder, the insulation mat extending between a first surface and a second surface, a veil attached to the first surface, the veil structured to inhibit physical movement of the cured combination through the veil, a metal sheet attached to the second surface by a water-containing adhesive contacting the metal sheet and the second surface, and a corrosion inhibitor composition deposited on the cured combination of the insulation mat, the corrosion inhibitor composition being effective to modify toward neutral a pH of the cured combination in contact with water from the water-containing adhesive.

BACKGROUND OF THE INVENTION

The present application relates generally to insulation materials orarticles of manufacture including corrosion inhibitors and methods ofproducing the same. To form mineral wool insulation materials andarticles, such as those comprising fiberglass and/or rock wool, one ormore binder compositions may be combined with mineral wool fibers andthe binder/fiber combination may be cured to provide an insulation mat.The inventors have discovered that the characteristics of various curedbinder/fiber compositions may contribute to undesired consequences incertain applications. For example, the pH characteristics of curedbinder/fiber compositions may accelerate or contribute to corrosion orhazing of metal material which come into contact with or proximity withcured binder/fiber compositions. As one non-limiting example, duct linerarticles may be constructed by affixing one side of an insulation matcomprising a cured binder/fiber combination to a metal sheet andaffixing a veil to an opposite side of the mat. During production theshow side of the metal sheet (the side that would be visible in theultimate application) for one duct liner article may come into contactor proximity with the veil of another duct liner article resulting in acorrosion or hazing of the show side. This effect may occur even whensheet metal with a galvanized show side is utilized. There remains asignificant need for the unique insulation materials or articles ofmanufacture including corrosion inhibitors and methods of producing thesame disclosed herein.

For the purposes of clearly, concisely and exactly describing exemplaryembodiments of the invention, the manner and process of making and usingthe same, and to enable the practice, making and use of the same,reference will now be made to certain exemplary embodiments, includingthose illustrated in the figures, and specific language will be used todescribe the same. It shall nevertheless be understood that nolimitation of the scope of the invention is thereby created, and thatthe invention includes and protects such alterations, modifications, andfurther applications of the exemplary embodiments as would occur to oneskilled in the art.

SUMMARY OF THE INVENTION

Exemplary embodiments include unique insulation articles includingcorrosion inhibitors and methods of producing the same. One exemplaryembodiment is an article of manufacture comprising an insulation matcomprising a cured combination of a plurality of randomly orientedfibers and a binder, the insulation mat extending between a firstsurface and a second surface, a veil attached to the first surface, theveil structured to inhibit physical movement of the cured combinationthrough the veil, a metal sheet attached to the second surface by awater-containing adhesive contacting the metal sheet and the secondsurface, and a corrosion inhibitor composition deposited on the curedcombination of the insulation mat, the corrosion inhibitor compositionbeing effective to modify toward neutral a pH of the cured combinationin contact with water from the water-containing adhesive. Furtherembodiments, forms, objects, features, advantages, aspects, and benefitsshall become apparent from the following description and drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a partial side sectional view of a plurality of duct linerinsulation articles according to one embodiment.

FIG. 2 is a partial side sectional view of a plurality of duct linerinsulation articles according to another embodiment.

FIG. 3 is a partial side sectional view of a plurality of duct linerinsulation articles according to another embodiment.

FIG. 4 is a partial side sectional view of a plurality of duct linerinsulation articles according to another embodiment.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

With reference to FIG. 1 there is illustrated a duct liner insulationarticle 110 including an insulation mat 112 comprising a curedcombination of a plurality of randomly oriented fibers and a binder. Anumber of types of cured combinations may be utilized. The plurality ofrandomly oriented fibers may comprise mineral wool fibers such asfiberglass, rock wool or combinations thereof as well as other types ofrandomly oriented fibers. The binder may include one or more of a numberof binder compounds including, for example, phenol formaldehyde (PF)binders, acrylic binders, polyester-type binders (e.g. those based onmonomeric polycarboxylic acid and monomeric polyol, those based onpolymeric polycarboxylic acid and monomeric polyol, those based onmonomeric polycarboxylic acid and a polymeric polyol, or those based onpolymeric polycarboxylic acid and a polymeric polyol), MaillardChemistry based binders (e.g., Glucose/Ammonium Citrate,Glucose/Ammonium Sulfate, or Glucose/Ammonium Phosphates such asGlucose/Monoammonium Phosphate (MAP), Glucose/Diammonium Phosphate (DAP)or Glucose/Triammonium Phosphate (TAP)), or combinations of these andother binders.

In forming insulation mat 112 or more binder compositions is combinedwith a plurality of randomly oriented fibers and the binder/fibercombination is cured to bind the fibers and form the insulation mat 112.An uncured binder/fiber combination may be formed using a variety oftechniques including, for example, using a spinner to form fibers frommolten precursor material, admixing one or more binder compositions withthe fibers, and collecting or aggregating the binder/fiber combination.The chemical reaction involved in curing the binder/fiber combinationmay require or may perform best under particular conditions. Forexample, a number of preferred binder curing chemistries require orperform best under acidic pH curing conditions, whereas a number ofothers require or perform best under alkaline or basic pH curingconditions. Table 1 below lists a number of non-limiting examples ofbinder chemistries which may be utilized in forming insulation mat 112and the pH of each binder in an uncured state (“pH of Binder) and the pHof an aqueous extract of the cured binder.

TABLE 1 pH of pH of Aqueous Uncured Extract of Ex. # Binder ChemistryBinder Cured Binder 1 Phenol-Formaldehyde Alkaline Acidic, Neutral, orAlkaline 2 Acrylic Acidic Acidic or Neutral 3 Maillard Reaction AlkalineAcidic (Ammonium Sulfate) 4 Maillard Reaction Alkaline Acidic(Diammonium Phosphate) 5 Polyester based on Acidic Acidic, Neutral,polycarboxylic acid and or Alkaline polyol

It shall be appreciated that for some binders the pH of an aqueousextract of the binder may change significantly depending on the degreeof cure is extended. Table 2A below describes the pH change for a numberof different exemplary binder formulations (A-H) as a function of curetemperature (ranging from 350 F to 450 F) and cure time (ranging from 5minutes to 30 minutes) as well as the pH at the start of cure, the pH atthe end of cure and the solubility characteristics of the binder atvarious degrees of curing. Table 2B below provides details as to theformulation of binders A-H.

TABLE 2A Degree of Binder Cure (Temperature/Time) Binder Binder pH350F/5m 400F/5m 400F/10m 400F/20m 400F/30m 400F/30m Start pH End pH A9.68 6.75^(#) 5.15^(#) 1.74* 1.68* 2.20* 2.33* Basic Acidic B 6.956.55^(#) 6.22^(#) 2.99** 2.40* 3.30* 3.15* Basic Acidic C 9.40 6.36^(#)5.85^(#) 6.80* 9.11* 9.00* 9.59* Basic Neutral- Basic D 7.80 8.16^(#)7.90^(#) 8.05** 9.47* 10.03* 9.88* Basic Basic E 4.00 4.05^(#) 4.02^(#)4.05^(#) 2.53* 5.95* 6.93* Acidic Neutral F 4.75 4.70^(#) 4.70^(#)4.75^(#) 6.12* 6.65* 7.08* Acidic Neutral G 1.65 2.05^(#) 2.02^(#)2.15^(#) 2.55* 3.80* 6.12* Acidic Acidic- Neutral H 4.00 4.02^(#)4.02^(#) 4.15^(#) 7.50* 8.50* 8.42* Acidic Basic ^(#) = binder watersoluble * = binder water soluble ** = binder partially water soluble

TABLE 2B Binder Constituents** Solids Ratio Amount (g) A Water 115.63Dextrose 90.9% 80.34 82.44 AS 40.0% 16.82 39.22 NH3 19.0% 2.52 12.37 BWater 148.01 Dextrose 90.9% 76.4 95.3 DAP 100.0%  5.57 6.32 C Water46.07 PF-Urea 47.1% 100 186.09 AS 40.0% 4.5 9.86 NH3 19.0% 1.68 7.75 DWater 79.1 SMA 49.0% 324.97 152.18 TEA 100.0%  81.57 18.72 E Water 81.87PAA 48.0% 100 143.94 Glycerol 100.0%  35 24.18 F Water 81.87 PAA 48.0%100 143.94 TEA 100.0%  35 24.18 G Water 156.72 CA 100.0%  100 46.64Glycerol 100.0%  100 46.64 H Water 156.72 CA 100.0%  100 46.64 TEA100.0%  100 46.64 **all binder formulations prepared as 37.31% bindersolids AS = Ammonium Sulfate NH3 = Ammonia DAP = Diammonium PhosphatePF-Urea: GP 2894 Resin pre-reacted with Urea in a 70/30 blend AS =Ammounium Sulfate NH3 = Ammonia SMA = Polyscope XIRAN Binder 204 TEA =Triethanolamine PAA = Rohm & Haas Acumer 1000 PAA = Rohm & Haas Acumer1000 TEA = Triethanolamine CA = Citric Acid CA = Citric Acid TEA =Triethanolamine

The required or preferred curing pH conditions for various bindersresult in cured binder/fiber compositions having particularcharacteristics. A number of cured binder/fiber combinations have anacidic pH including, such as the examples listed in Tables 1, 2A and 2Babove. A number of other cured binder/fiber combinations may have analkaline pH including, such as the examples listed in Tables 1, 2A and2B above. It shall be appreciated that the pH of a cured binder/fibercombination may be characterized by a number of techniques includingperforming a pH measurement (e.g. with a pH meter or pH chemical teststrip) of a resulting aqueous solution when the cured binder/fibercombination is immersed in deionized water.

In the embodiment illustrated in FIG. 1, a corrosion inhibitor 113 isdeposited and on a first side of insulation mat 112 after thebinder/fiber combination has been cured. This avoids interference by thecorrosion inhibitor 113 with the curing reaction of the binder/fibercomposition. Corrosion inhibitor 113 may be applied to the curedbinder/fiber combination using a number of techniques including, forexample, as an aqueous spray, as a liquid, as a slurry, or as a powder.It shall be appreciated that the application technique may be selectedbased upon considerations such as the solubility characteristics of aparticular corrosion inhibitor and the particular application devicesand equipment which are preferred for a given production process.

The chemical composition of corrosion inhibitor 113 is preferablyselected to provide at least one of a pH neutralization effect relativeto the characteristics of the cured binder/fiber combination ofinsulation mat 112, a passivation effect relative to a metal surfacewhich may come into contact or proximity with the duct liner insulationarticle 110, or a combination of both effects. Accordingly, corrosioninhibitor 113 may comprise a number of different chemical compositionsdepending on the characteristics of the cured binder/fiber combinationof insulation mat 112. For cured binder/fiber combinations having anacidic pH, one or more chemical compound providing an alkaline pH may beselected as the corrosion inhibitor 113. Table 3 below lists a number ofpreferred alkaline corrosion inhibitors and their water solubilitycharacteristics.

TABLE 3 Solubility Ex. # Alkaline Corrosion Inhibitor Characteristic 1.sodium hydroxide water soluble 2. sodium carbonate water soluble 3.sodium bicarbonate water soluble 4. potassium hydroxide water soluble 5.potassium carbonate water soluble 6. potassium carbonate water soluble7. ammonium carbonate. water soluble 8. ammonium bicarbonate watersoluble 9. monoethanolamine water soluble 10. diethanolamine watersoluble 11. triethanolamine water soluble 12. zinc phophate essentiallywater insoluble 13. calcium phosphate essentially water insoluble 14.long chain alkyl imidazoline (e.g. those essentially water offeredcommercially by Lonza under insoluble the registered trademarksUNAMINE ® O and UNAMINE ® C)

In forms where a corrosion inhibitor with an alkaline pH is selected,the corrosion inhibitor 113 may comprise one or more of the alkalinecorrosion inhibitors listed in Table 3 above as well as combinationsthereof. In further forms where a corrosion inhibitor with an alkalinepH is selected, the corrosion inhibitor 113 may consist essentially ofany of the alkaline corrosion inhibitors listed in Table 3 above or mayconsist essentially of a combination of two or more of the alkalinecorrosion inhibitors listed in Table 3 above. It shall be furtherappreciated that other alkaline corrosion inhibitors may also beutilized in addition to or instead of the non-limiting examplesdisclosed herein.

For cured binder/fiber combinations having an alkaline pH, one or morechemical compound providing an acidic pH may be selected as thecorrosion inhibitor 113. Table 4 below lists a number of preferredacidic corrosion inhibitors.

TABLE 4 Ex. # Acidic Corrosion Inhibitor 1. Tetraaquahydrogen 2. SodiumBicarbonate 3. Potassium Bicarbonate 4. Magnesium Bicarbonate 5. CalciumBicarbonate 6. Ammonium Bicarbonate

In forms where a corrosion inhibitor with an acidic pH is selected, thecorrosion inhibitor 113 may comprise one or more of the acidic corrosioninhibitors listed in Table 4 above as well as combinations thereof. Infurther forms where a corrosion inhibitor with an acidic pH is selected,the corrosion inhibitor 113 may consist essentially of any of the acidiccorrosion inhibitors listed in Table 4 above or may consist essentiallyof a combination of two or more of the acidic corrosion inhibitorslisted in Table 4 above. It shall be further appreciated that otheracidic corrosion inhibitors may also be utilized in addition to orinstead of the non-limiting examples disclosed herein.

It shall be appreciated that the physical location and extent of thecorrosion inhibitor 113 is shown generally in FIG. 1 for purposes ofillustration and that a number of particular locations and extents arecontemplated. In certain forms the corrosion inhibitor 113 may bedeposited and positioned substantially entirely on the surface of thefirst side of insulation mat 112. In certain forms the corrosioninhibitor 113 may be deposited on the surface of the first side ofinsulation mat 112 and may also extend into the insulation mat 112. Thedegree to which the corrosion inhibitor 113 extends into the insulationmat 112 may vary depending upon the form in which the corrosioninhibitor is applied (e.g., powder form, liquid, aqueous solution,slurry), amount of corrosion inhibitor applied, and the applicationtechnique utilized to apply the corrosion inhibitor. For certainpreferred spray on applications inhibitors in the 0.1 to 2 g/ft² ofactive ingredient have been found effective. Exemplary corrosioninhibitors which are effective in this range include Sodium Carbonate(NaCO₃), Potassium Hydroxide (KO-f), Triethanolamine (TEA),2-Nitrophenol, Sodium Molybdate (Na₂MoO₄) and Cerium Chloride (CeCl₃).

As further illustrated in FIG. 1, a veil 111 is affixed to the firstside of insulation mat 112. Veil 111 is preferably structured to inhibitphysical movement of the cured binder/fiber combination past veil 111while allowing the passage of vapor or liquid. It shall be appreciatedthat veil 111 may not entirely prevent physical movement of the curedbinder/fiber composition and may permit the passage of some amount ofthe cured binded/fiber composition (e.g., a small amount of loose fiber)through veil 111. In certain preferred forms veil 11 may comprise afiberglass veil, or blends of glass and thermoplastic elastomeric (TPE)fibers such as veils comprising combinations or blends of fiberglass andpolyester. Veil 111 may be affixed to the first side of insulation matusing an adhesive. A water based adhesive is preferred although a hotmelt adhesive or a non-water based adhesive may also be utilized. Avariety of water based adhesives may be utilized. It shall beappreciated that the water based adhesive is preferably selected to havea pH which is either neutral or which corresponds to the pH of theselected corrosion inhibitor. Thus, acidic to neutral pH adhesives arepreferred for use in combination with acidic corrosion inhibitors, andalkaline to neutral pH adhesives are preferred for use in combinationwith alkaline corrosion inhibitors.

The second side of insulation mat 112 is affixed to metal sheet 115 byadhesive 114 which may be a water containing adhesive such as the VAElaminating adhesive 82000 adhesive offered commercially by EFI Polymers.Other suitable adhesives types include, without limitation, water-bornadhesives, latex emulsions, e.g. Polyvinyl acetate (PVA) emulsions,polyacrylate emulsions, Ethylene Vinyl acetate (EVA) emulsion, andStyrene-Butadiene emulsions. Metal sheet 115 may be a steel sheet, astainless steel sheet, or a galvanized steel sheet. It shall beappreciated that the physical location and extent of the adhesive isshown generally in FIG. 1 and that a number of particular locations andextents are contemplated. In one non limiting example, 82000 adhesivewas applied at a rate of 60 g/ft2 to a galvanized steel sheet to affixedan one inch thickness insulation mat comprising a cured combination offiberglass and a dextrose diammonium phosphate (DAP) binder with anall-glass veil affixed to the insulation mat.

FIG. 1 further illustrates duct liner insulation article 120 whichincludes insulation mat 122, corrosion inhibitor 123, veil 121, adhesive124 and metal sheet 125. The characteristics and properties of thesecomponents of duct liner insulation article 120 may be substantially thesame as insulation mat 112, corrosion inhibitor 113, veil 111, adhesive114 and metal sheet 115 of duct liner insulation article 110 asdescribed above.

Duct liner insulation articles 110 and 120 of the various compositionsand combinations described herein above may be produced according to aprocess including the following operations: (a) forming an insulationmat comprising an uncured of binder/fiber combination, (b) curing theinsulation mat to provide a cured binder/fiber combination. (c) applyinga corrosion inhibitor composition to a first side of the curedinsulation mat, (d) affixing a veil to the first side of the insulationmat with a first adhesive. (e) affixing the second side of theinsulation mat to a metal sheet with a second adhesive, (f) repeatingprocess operations (a) through (e) to provide a plurality of articles,(g) positioning the resulting articles in contact or proximity with oneanother, (h) allowing the second adhesive to set for a predeterminedperiod of time, and (i) further forming duct structures using one ormore articles.

The configuration illustrated in FIG. 1 depicts portions of a pluralityof duct liner insulation articles including article 110 and article 120which are positioned in a stack with veil 121 contacting a show side ofmetal sheet 115 at interface 150. As indicated by ellipsis 130additional duct liner insulation articles may also be provided in thestack. It shall be further appreciated that the stacked position ofarticle 110 and article 120 is one non-limiting example of aconfiguration in which a portion of one duct liner insulation articlemay be in contact with or proximity with a portion of another duct linerinsulation article. In other configurations, adjacent articles may bespaced apart or may be in contact with one another over certain regionsand spaced apart in other regions. The illustrated configuration is butone example of a configuration presenting potential for undesiredconsequences such as hazing, corrosion, or other chemical reactionsaffecting the show side of a duct liner insulation article.

Without wishing to be limited to particular mechanisms of action orefficacy, the theory underlying certain exemplary mechanisms shall nowbe-described. The structure and composition of articles 110 and 120 arebelieved to mitigate the potential for undesired consequences such ashazing, corrosion, or other chemical reactions affecting the show sideof a duct liner insulation article by a pH neutralization effectrelative to the characteristics of the cured binder/fiber combination ofinsulation mat 112, a passivation effect relative to the show side ofmetal sheet 115, or a combination of both effects. After articles 110and 120 are initially assembled, adhesives 113 and 123 transition from awet or unfixed state to a dried or fixed state over a period of time.Moisture from adhesive 113 and 123 may travel through insulation mats112 and 122, respectively. As this moisture interacts with the curedbinder/fiber combination an acidic or alkaline pH may be imparted to themoisture. The pH neutralization effect of corrosion inhibitors 113 and123 is believed to modify the pH of the moisture in contact with thecured binder/fiber combination toward neutral by providing an opposingpH providing a neutralizing reaction. The passivation effect ofcorrosion inhibitors 113 and 123 is believed to involve movement of thecorrosion inhibitor through the insulation mats 112 and 122 and veils111 and 121 to contact an adjacent metal surface where the corrosioninhibitor passivates the metal surface by chemically interacting withbinding sites that might otherwise be reactive to the pH of the curedbinder/fiber composition.

In certain embodiments including galvanized metal sheets a particularmechanism of action is believed to occur. It believed that in suchembodiments an initially shiny metal surface of the zinc metal reactswith the moisture to form hydrated zinc oxides. The surface areas incontact with moisture become dull and also form white haze. Theappearance of the surface is non-uniform and is objectionable,especially in those cases where the affected surface is an exposedsurface or show side in construction applications. Mitigating theseissues is not simple or straightforward. On complication is that thepresence of acidic or alkaline compounds, such as the disclosedcorrosion inhibitors, may themselves provide undesired corrosion orreactions producing similar results. Another complication is that thecorrosion inhibitors themselves may produce objectionable results, forexample, providing a non-uniform or blemished surface when applieddirectly to a metal surface or directly onto the surface of an adjacentarticle that comes in contact of the galvanized steel. In thoseinstances the applied corrosion inhibitors typically form a film orcrust on the galvanized steel surface which is undesirable. In theseembodiments a surprising result occurred by application of the corrosioninhibitor as illustrated in FIG. 1. While the corrosion inhibitor wasfree to pass through the veil and in theory produce the pHneutralization and/or passivation effect as well as the undesiredresults noted above, it was observed in practice that the beneficialeffects were present whereas the undesired effects and complicationswere not.

With reference to FIG. 2 there is illustrated another embodimentcomprising a plurality of duct liner insulation articles including ductliner insulation articles 210 and 220. It is contemplated thatadditional duct liner insulation articles may also be included asindicated by ellipsis 230. Articles 210 and 220 include a numbercomponents which may have the same or similar characteristics andproperties as corresponding components illustrated and described abovein connection with FIG. 1. In FIG. 2 corresponding components arelabeled with references numerals incremented by 100 relative to those ofFIG. 1. Thus, insulation mat 212, corrosion inhibitor 213, veil 211,adhesive 214 and metal sheet 215 of article 210 correspond to insulationmat 112, corrosion inhibitor 113, veil 111, adhesive 114 and metal sheet115 of article 110, respectively. Similarly, insulation mat 222,corrosion inhibitor 223, veil 221, adhesive 224 and metal sheet 225 ofarticle 220 correspond to insulation mat 122, corrosion inhibitor 123,veil 121, adhesive 124 and metal sheet 125 of article 120, respectively.Likewise, ellipsis 230 corresponds to ellipsis 130, and interface 250corresponds to interface 150. The different forms, compositions,variations and alternative described in connection with the embodimentof FIG. 1 also apply to the embodiment of FIG. 2.

It shall be appreciated that the embodiment of FIG. 2 differs from theembodiment of FIG. 1 in certain respects which shall now be described.In the embodiment illustrated in FIG. 2, corrosion inhibitor 213 isdeposited on the bottom side of insulation mat 212 which faces adhesive214 and metal sheet 215. This configuration permits veil 211 to beaffixed to the top side of insulation mat 212 using additionaltechniques. In one non-limiting example, insulation mat 212 mayinitially comprise an uncured binder/fiber combination, veil 211 may beplaced on the upper side of insulation mat 212 in the uncured state, andthe insulation mat 212 and veil 211 may be cured in this configurationeffective to affix veil 211 to insulation mat 212. After curing,corrosion inhibitor 213 may be applied to the bottom side of insulationmat 212 using any of the techniques disclosed above in connection withFIG. 1. The bottom side of insulation mat 212 may then be affixed tometal sheet 215 with adhesive 214. In certain preferred forms the amountof corrosion inhibitor applied to the bottom side of insulation mat 212and/or the degree of penetration into insulation mat 212 may be the sameas or may be increased relative to the embodiment illustrated in FIG. 1.

Duct liner insulation articles 210 and 220 of the various compositionsand combinations described herein above may be produced according to aprocess including the following operations: (a) forming an insulationmat comprising an uncured of binder/fiber combination, (b) applying aveil to the first side of the insulation mat. (c) curing the insulationmat in contact with the veil to provide a cured binder/fiber combinationaffixed to the veil, (d) applying a corrosion inhibitor composition tothe second side of the cured insulation mat. (e) affixing the secondside of the insulation mat to a metal sheet with an adhesive, (f)repeating process operations (a) through (e) to provide a plurality ofarticles. (g) positioning the resulting articles in contact with orproximity with one another, (h) allowing the adhesive to set for apredetermined period of time, and (i) further forming duct structuresusing one or more articles.

It shall be appreciated that alternate techniques and order ofoperations for applying the veil may be utilized including, for example,those described above in connection with FIG. 1. It shall be furtherappreciated that the structure and composition of articles 210 and 220are believed to mitigate the potential for undesired consequences suchas hazing, corrosion, or other chemical reactions affecting the showside of a duct liner insulation article by a pH neutralization effectrelative to the characteristics of the cured binder/fiber combination ofthe insulation mats and a passivation effect relative to the show sideof adjacent metal sheet, or a combination of both effects. These effectsmay have the characteristics described above in connection with FIG. 1.

With reference to FIG. 3 there is illustrated another embodimentcomprising a plurality of duct liner insulation articles including ductliner insulation articles 310 and 320. It is contemplated thatadditional duct liner insulation articles may also be included asindicated by ellipsis 330. Articles 310 and 320 include a numbercomponents which may have the same or similar characteristics andproperties as corresponding components illustrated and described abovein connection with FIG. 1. In FIG. 3 corresponding components arelabeled with references numerals incremented by 200 relative to those ofFIG. 1. Thus, insulation mat 312, corrosion inhibitor 313, veil 311,adhesive 314 and metal sheet 315 of article 310 correspond to insulationmat 112, corrosion inhibitor 113, veil 111, adhesive 114 and metal sheet115 of article 110, respectively. Similarly, insulation mat 322,corrosion inhibitor 323, veil 321, adhesive 324 and metal sheet 325 ofarticle 320 correspond to insulation mat 122, corrosion inhibitor 123,veil 121, adhesive 124 and metal sheet 125 of article 120, respectively.Likewise, ellipsis 330 corresponds to ellipsis 130, and interface 350corresponds to interface 150. The different forms, compositions,variations and alternative described in connection with the embodimentof FIG. 1 also apply to the embodiment of FIG. 3.

It shall be appreciated that the embodiment of FIG. 3 differs from theembodiment of FIG. 1 in certain respects which shall now be described.In the embodiment illustrated in FIG. 3, corrosion inhibitor 313 isdeposited at a plurality of locations within the thickness of curedinsulation mat 312. This configuration permits veil 311 to be affixed tothe top side of insulation mat 312 using any of the techniques describedabove in connection with FIGS. 1 and 2. Corrosion inhibitor 313 may beapplied to the plurality of locations within insulation mat 312 using anumber of techniques. Exemplary techniques include apparatuses includinginjection or application needles or nozzles which penetrate into thethickness of insulation mat 312 to various predetermined depths and jetspray injectors which direct a stream of corrosion inhibitor thatpenetrates into the thickness of the insulation mat. These applicationtechniques may penetrate into either side of insulation mat 312. Thecorrosion inhibitor 313 may be applied prior to or after veil 311 isaffixed to the insulation mat 312. Likewise, the corrosion inhibitor 313may be applied prior to or after the insulation mat 312 is affixed tometal sheet 315. The bottom side of insulation mat 312 may be affixed tometal sheet 315 with adhesive 314.

Duct liner insulation articles 310 and 320 of the various compositionsand combinations described herein above may be produced according to aprocess including the following operations: (a) forming an insulationmat comprising an uncured of binder/fiber combination, (b) applying aveil to the first side of the insulation mat, (c) curing the insulationmat in contact with the veil to provide a cured binder/fiber combinationaffixed to the veil, (d) applying a corrosion inhibitor composition atinterior locations in the insulation mat using techniques such aspenetrating injection needles, penetrating injection nozzles, orpenetrating sprays, (e) affixing the second side of the insulation matto a metal sheet with an adhesive, (f) repeating process operations (a)through (e) to provide a plurality of articles, (g) positioning theresulting articles in contact with or proximity with one another, (h)allowing the adhesive to set for a predetermined period of time, and (i)further forming duct structures using one or more articles.

It shall be appreciated that alternate techniques and order ofoperations for applying the veil may be utilized including, for example,those described above in connection with FIG. 1. In another variation,operation (e) may be performed prior to operation (d). It shall befurther appreciated that the structure and composition of articles 310and 320 are believed to mitigate the potential for undesiredconsequences such as hazing, corrosion, or other chemical reactionsaffecting the show side of a duct liner insulation article by a pHneutralization effect relative to the characteristics of the curedbinder/fiber combination of the insulation mats and a passivation effectrelative to the show side of adjacent metal sheet, or a combination ofboth effects. These effects may have the characteristics described abovein connection with FIG. 1.

With reference to FIG. 4 there is illustrated another embodimentcomprising a plurality of duct liner insulation articles including ductliner insulation articles 410 and 420. It is contemplated thatadditional duct liner insulation articles may also be included asindicated by ellipsis 430. Articles 410 and 420 include a numbercomponents which may have the same or similar characteristics andproperties as corresponding components illustrated and described abovein connection with FIG. 1. In FIG. 4 corresponding components arelabeled with references numerals incremented by 300 relative to those ofFIG. 1. Thus, insulation mat 412, corrosion inhibitor 413, veil 411,adhesive 414 and metal sheet 415 of article 410 correspond to insulationmat 112, corrosion inhibitor 113, veil 111, adhesive 114 and metal sheet115 of article 110, respectively. Similarly, insulation mat 422,corrosion inhibitor 423, veil 421, adhesive 424 and metal sheet 425 ofarticle 420 correspond to insulation mat 122, corrosion inhibitor 123,veil 121, adhesive 124 and metal sheet 125 of article 120, respectively.Likewise, ellipsis 430 corresponds to ellipsis 130, and interface 450corresponds to interface 150. The different forms, compositions,variations and alternative described in connection with the embodimentof FIG. 1 also apply to the embodiment of FIG. 4.

It shall be appreciated that the embodiment of FIG. 4 differs from theembodiment of FIG. 1 in certain respects which are similar to thedifferences described above in connection with FIG. 3. In the embodimentof FIG. 4 the corrosion inhibitor 413 may be deposited using techniquessimilar to those described above in connection with FIG. 3. The positionof corrosion inhibitor 413 differs in that it is controlled to be atlocations within insulation mat 412 that are proximate veil 411. Thismay be accomplished by varying the depth or penetration of theapplication needle or nozzle or the intensity of the penetrating jetspray. The production processes described above in connection with FIG.3 may also be utilized for production of the articles illustrated in theembodiment of FIG. 4.

While the invention has been illustrated and described in detail in thedrawings and foregoing description, the same is to be considered asillustrative and not restrictive in character, it being understood thatonly certain exemplary embodiments have been shown and described andthat all changes and modifications that come within the spirit of theinventions are desired to be protected. It should be understood thatwhile the use of words such as preferable, preferably, preferred or morepreferred utilized in the description above indicate that the feature sodescribed may be more desirable, it nonetheless may not be necessary andembodiments lacking the same may be contemplated as within the scope ofthe invention, the scope being defined by the claims that follow. Inreading the claims, it is intended that when words such as “a,” “an,”“at least one,” or “at least one portion” are used there is no intentionto limit the claim to only one item unless specifically stated to thecontrary in the claim. When the language “at least a portion” and/or “aportion” is used the item can include a portion and/or the entire itemunless specifically stated to the contrary.

1. An article of manufacture comprising: an insulation mat comprising acured combination of a plurality of randomly oriented fibers and abinder, the insulation mat extending between a first surface and asecond surface; a veil attached to the first surface, the veilstructured to inhibit physical movement of the cured combination throughthe veil; a metal sheet attached to the second surface by awater-containing adhesive contacting the metal sheet and the secondsurface; and a corrosion inhibitor composition deposited on the curedcombination of the insulation mat, the corrosion inhibitor compositionbeing effective to modify toward neutral a pH of the cured combinationin contact with water from the water-containing adhesive.
 2. The articleof manufacture of claim 1 wherein the article of manufacture comprisesat least one of the following features: wherein the cured combinationhas an acidic pH and the corrosion inhibitor composition has an alkalinepH, wherein the corrosion inhibitor composition comprises a watersoluble compound, wherein the water soluble compound comprises at leastone of sodium hydroxide, sodium carbonate, sodium bicarbonate, potassiumhydroxide, potassium carbonate, potassium bicarbonate, ammoniumcarbonate, ammonium bicarbonate, monoethanolamine, diethanolamine, andtriethanolamine, wherein the corrosion inhibitor composition comprisesan essentially water insoluble compound, wherein the corrosion inhibitorcomposition comprises an essentially water insoluble compound and theessentially water insoluble compound comprises at least one of zincphosphate, calcium phosphate, and a long chain alkyl imidazoline. 3.-6.(canceled)
 7. The article of manufacture of claim 1 wherein thecorrosion inhibitor composition is deposited on the first surface of theinsulation mat.
 8. The article of manufacture of claim 1 wherein thearticle of manufacture comprises at least one of the following features:wherein the binder is a non-phenol formaldehyde (PF) composition,wherein the binder comprises one of an acrylic binder, a polyester-typebinder, a binder which includes at least one reaction product from aMaillard reaction, and a combination thereof, wherein the bindercomprises a polyester-type binder based upon one of: a monomericpolycarboxylic acid and a monomeric polyol, a polymeric polycarboxylicacid and a monomeric polyol, a monomeric polycarboxylic acid and apolymeric polyol, and a polymeric polycarboxylic acid and a polymericpolyol. 9.-10. (canceled)
 11. The article of manufacture of claim 1wherein the article of manufacture comprises at least one of thefollowing features: wherein the binder comprises at least one reactionproduct from a Maillard reaction, wherein the binder comprises at leastone reaction product from a Maillard reaction and wherein the reactionproduct comprises at least one product of a reducing sugar and an aminereactant, wherein the binder comprises at least one reaction productfrom a Maillard reaction and wherein the reaction product comprises atleast one product of a carbohydrate reactant and a polycarboxylic acidammonium salt reactant. 12.-13. (canceled)
 14. The article ofmanufacture of claim 1 wherein the metal sheet is a galvanized metalsheet.
 15. The article of manufacture of claim 1 wherein the pluralityof randomly oriented fibers are one of fiberglass fibers and rock woolfibers.
 16. An article of manufacture comprising: an insulation matcomprising a cured combination of a plurality of randomly orientedfibers and a binder, the insulation mat extending between a firstsurface and a second surface, the cured combination having one of anacidic pH and an alkaline pH when immersed in deionized water; a veilattached to the first surface, the veil structured to inhibit physicalmovement of the cured combination through the veil; and a corrosioninhibitor composition deposited on the cured combination of theinsulation mat, the corrosion inhibitor composition having the oppositeof the one of the acidic pH and the alkaline pH of the cured compositionwhen immersed in deionized water.
 17. The article of manufacture ofclaim 16 wherein the article of manufacture comprises at least one ofthe following features: wherein the article of manufacture furthercomprises a metal sheet attached to the second surface by awater-containing adhesive contacting the metal sheet and the secondsurface, wherein the corrosion inhibitor composition is effective tomodify toward neutral a pH of the cured combination in contact withwater from the water-containing adhesive, wherein the veil is positionedin contact with a surface of a second metal sheet, wherein the veil ispositioned in contact with a surface of a second metal sheet and whereinthe corrosion inhibitor composition provides passivation of the surfaceof the second metal sheet, wherein the veil is positioned in contactwith a surface of a second metal sheet and wherein the corrosioninhibitor composition provides passivation of the surface of the secondmetal sheet and wherein the surface of the second metal sheet isgalvanized, wherein the binder comprises at least one reaction productfrom a Maillard reaction, the cured composition has an acidic pH, andthe corrosion inhibitor composition has an alkaline pH. 18.-22.(canceled)
 23. A method comprising: providing an insulation matcomprising a cured combination of a plurality of randomly orientedfibers and a binder and a veil attached to a first surface of the curedcombination and effective to inhibit physical movement of the curedcombination through the veil; applying a corrosion inhibitor compositionto the cured combination of the insulation mat; attaching a metal sheetto a second surface of the cured combination with a water-containingadhesive contacting the metal sheet and the second surface; andcontacting the veil with a second metal sheet; wherein the corrosioninhibitor composition is effective to inhibit a reaction of water fromthe water-containing adhesive, the cured combination and the secondmetal sheet.
 24. The method of claim 23 wherein the method comprises atleast one of the following features: wherein the corrosion inhibitorcomposition is effective to modify toward neutral a pH of the curedcombination in contact with water from the water-containing adhesive,wherein the corrosion inhibitor composition is effective to passivate asurface of the second metal sheet, wherein the act of providing aninsulation mat includes curing the binder in combination with theplurality of randomly oriented fibers with the veil contacting the firstsurface effective to provide the cured combination and to attach theveil to the first surface, wherein the act of applying comprisesapplying the corrosion inhibitor composition to a second surface of thecured combination of the insulation mat, the second surface beingopposite from the first surface, wherein the corrosion inhibitorcomposition is applied to the second surface by spraying one of anaqueous solution including the corrosion inhibitor composition and anaqueous slurry including the corrosion inhibitor composition. 25.-28.(canceled)
 29. A method comprising: forming an insulation mat comprisinga combination of a plurality of randomly oriented fibers and a binder,the insulation mat extending between a first side and a second side;applying a veil to the first side of the insulation mat; curing theinsulation mat and the veil effective to bind the plurality of randomlyoriented fibers and to bind the veil to the first side; and applying acorrosion inhibitor composition to the second side of the insulationmat; wherein the cured combination has one of an acidic pH and analkaline pH when immersed in deionized water, and the corrosioninhibitor composition has the other of the acidic pH and the alkaline pHwhen immersed in deionized water.
 30. The method of claim 29 furthercomprising: attaching a first metal sheet to the second side of theinsulation mat with a water-containing adhesive contacting the metalsheet and the second surface; and contacting the veil with a surface ofa second metal sheet; wherein the corrosion inhibitor composition iseffective to inhibit a reaction of water from the water-containingadhesive, the cured combination and the second metal sheet.
 31. Themethod of claim 30 wherein the method comprises at least one of thefollowing features: wherein the surface of the second metal sheetcontacting the veil is galvanized, wherein the corrosion inhibitorcomposition modifies toward neutral a pH of the cured combination incontact with water from the water-containing adhesive, wherein thecorrosion inhibitor passivates the surface of the second metal sheet,wherein the binder comprises one of an acrylic binder, a polyester-typebinder, a binder which includes at least one reaction product from aMaillard reaction, and a combination thereof. 32.-34. (canceled)